EN 1.0920 steel belongs to the iron alloys classification, while N06210 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0920 steel and the bottom bar is N06210 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 23
51
Fatigue Strength, MPa 270
320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
85
Shear Strength, MPa 340
560
Tensile Strength: Ultimate (UTS), MPa 540
780
Tensile Strength: Yield (Proof), MPa 380
350

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1570
Melting Onset (Solidus), °C 1420
1510
Specific Heat Capacity, J/kg-K 470
420
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
85
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.6
17
Embodied Energy, MJ/kg 22
250
Embodied Water, L/kg 50
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
320
Resilience: Unit (Modulus of Resilience), kJ/m3 380
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
21
Thermal Shock Resistance, points 17
22

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.015
Chromium (Cr), % 0 to 0.3
18 to 20
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 96.1 to 99.08
0 to 1.0
Manganese (Mn), % 0.9 to 1.7
0 to 0.5
Molybdenum (Mo), % 0 to 0.1
18 to 20
Nickel (Ni), % 0 to 0.5
54.8 to 62.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.080
Sulfur (S), % 0 to 0.030
0 to 0.020
Tantalum (Ta), % 0
1.5 to 2.2
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.12
0 to 0.35