EN 1.0920 Steel vs. Z20301 Zinc

EN 1.0920 steel belongs to the iron alloys classification, while Z20301 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0920 steel and the bottom bar is Z20301 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 23
53
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
35
Tensile Strength: Ultimate (UTS), MPa 540
160
Tensile Strength: Yield (Proof), MPa 380
130

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 400
90
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1420
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 50
110
Thermal Expansion, µm/m-K 12
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
37

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
11
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 1.6
2.8
Embodied Energy, MJ/kg 22
53
Embodied Water, L/kg 50
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
78
Resilience: Unit (Modulus of Resilience), kJ/m3 380
96
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
6.7
Strength to Weight: Bending, points 19
9.9
Thermal Diffusivity, mm2/s 14
44
Thermal Shock Resistance, points 17
5.0

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.010
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.35
0 to 0.0050
Iron (Fe), % 96.1 to 99.08
0 to 0.010
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.9 to 1.7
0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0 to 0.12
0
Zinc (Zn), % 0
99.853 to 100