EN 1.1122 Steel vs. R30816 Cobalt

EN 1.1122 steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.1122 steel and the bottom bar is R30816 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 130
280
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 12 to 21
23
Fatigue Strength, MPa 170 to 260
250
Poisson's Ratio 0.29
0.3
Reduction in Area, % 63 to 73
22
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 340 to 460
1020
Tensile Strength: Yield (Proof), MPa 240 to 370
460

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1460
1540
Melting Onset (Solidus), °C 1420
1460
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 51
13
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.1
Embodied Carbon, kg CO2/kg material 1.4
20
Embodied Energy, MJ/kg 18
320
Embodied Water, L/kg 46
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 36 to 89
190
Resilience: Unit (Modulus of Resilience), kJ/m3 160 to 360
510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 12 to 16
31
Strength to Weight: Bending, points 14 to 17
25
Thermal Diffusivity, mm2/s 14
3.3
Thermal Shock Resistance, points 11 to 15
28

Alloy Composition

Carbon (C), % 0.080 to 0.12
0.32 to 0.42
Chromium (Cr), % 0
19 to 21
Cobalt (Co), % 0
40 to 49.8
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 98.7 to 99.62
0 to 5.0
Manganese (Mn), % 0.3 to 0.6
1.0 to 2.0
Molybdenum (Mo), % 0
3.5 to 4.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 0
3.5 to 4.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Tantalum (Ta), % 0
3.5 to 4.5
Tungsten (W), % 0
3.5 to 4.5