EN 1.1152 Steel vs. N06045 Nickel

EN 1.1152 steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.1152 steel and the bottom bar is N06045 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 22
37
Fatigue Strength, MPa 190 to 300
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 290 to 340
470
Tensile Strength: Ultimate (UTS), MPa 400 to 550
690
Tensile Strength: Yield (Proof), MPa 270 to 440
270

Thermal Properties

Latent Heat of Fusion, J/g 250
350
Maximum Temperature: Mechanical, °C 400
1010
Melting Completion (Liquidus), °C 1460
1350
Melting Onset (Solidus), °C 1420
1300
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
42
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
6.9
Embodied Energy, MJ/kg 18
98
Embodied Water, L/kg 46
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 41 to 110
200
Resilience: Unit (Modulus of Resilience), kJ/m3 200 to 530
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 14 to 19
24
Strength to Weight: Bending, points 15 to 19
22
Thermal Shock Resistance, points 13 to 17
18

Alloy Composition

Carbon (C), % 0.18 to 0.22
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 98.6 to 99.52
21 to 25
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Nickel (Ni), % 0
45 to 50.4
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.3
2.5 to 3.0
Sulfur (S), % 0 to 0.025
0 to 0.010