MakeItFrom.com
Menu (ESC)

EN 1.1181 Steel vs. AISI 304LN Stainless Steel

Both EN 1.1181 steel and AISI 304LN stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is AISI 304LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
190 to 350
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19 to 20
7.8 to 46
Fatigue Strength, MPa 190 to 260
200 to 440
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 350 to 390
400 to 680
Tensile Strength: Ultimate (UTS), MPa 560 to 620
580 to 1160
Tensile Strength: Yield (Proof), MPa 280 to 380
230 to 870

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 42
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 19
44
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
83 to 270
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
140 to 1900
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20 to 22
21 to 41
Strength to Weight: Bending, points 19 to 21
20 to 31
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19 to 21
13 to 26

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0 to 0.4
18 to 20
Iron (Fe), % 97.4 to 99.18
65 to 73.9
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
8.0 to 12
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030