EN 1.1181 Steel vs. AISI 316 Stainless Steel

Both EN 1.1181 steel and AISI 316 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is AISI 316 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
160 to 360
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19 to 20
8.0 to 55
Fatigue Strength, MPa 190 to 260
210 to 430
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 350 to 390
350 to 690
Tensile Strength: Ultimate (UTS), MPa 560 to 620
520 to 1180
Tensile Strength: Yield (Proof), MPa 280 to 380
230 to 850

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
590
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.9
Embodied Energy, MJ/kg 19
53
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
85 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
130 to 1820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20 to 22
18 to 41
Strength to Weight: Bending, points 19 to 21
18 to 31
Thermal Diffusivity, mm2/s 11
4.1
Thermal Shock Resistance, points 19 to 21
11 to 26

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.080
Chromium (Cr), % 0 to 0.4
16 to 18
Iron (Fe), % 97.4 to 99.18
62 to 72
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
2.0 to 3.0
Nickel (Ni), % 0 to 0.4
10 to 14
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030