EN 1.1181 Steel vs. AWS ER90S-B9

Both EN 1.1181 steel and AWS ER90S-B9 are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is AWS ER90S-B9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
18
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 560 to 620
690
Tensile Strength: Yield (Proof), MPa 280 to 380
470

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
25
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 19
37
Embodied Water, L/kg 47
91

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
570
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20 to 22
25
Strength to Weight: Bending, points 19 to 21
22
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 19 to 21
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0.32 to 0.39
0.070 to 0.13
Chromium (Cr), % 0 to 0.4
8.0 to 10.5
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 97.4 to 99.18
84.4 to 90.7
Manganese (Mn), % 0.5 to 0.8
0 to 1.2
Molybdenum (Mo), % 0 to 0.1
0.85 to 1.2
Nickel (Ni), % 0 to 0.4
0 to 0.8
Niobium (Nb), % 0
0.020 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 0.4
0.15 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.010
Vanadium (V), % 0
0.15 to 0.3
Residuals, % 0
0 to 0.5