EN 1.1181 Steel vs. EN 1.3570 Steel

Both EN 1.1181 steel and EN 1.3570 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is EN 1.3570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
150 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 560 to 620
490 to 1440

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
46
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20 to 22
17 to 51
Strength to Weight: Bending, points 19 to 21
18 to 36
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 19 to 21
14 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.32 to 0.39
0.17 to 0.23
Chromium (Cr), % 0 to 0.4
0.4 to 0.75
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 97.4 to 99.18
97.1 to 98.9
Manganese (Mn), % 0.5 to 0.8
0.65 to 1.1
Molybdenum (Mo), % 0 to 0.1
0.1 to 0.2
Nickel (Ni), % 0 to 0.4
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.035
0 to 0.030