EN 1.1181 Steel vs. EN 1.4404 Stainless Steel

Both EN 1.1181 steel and EN 1.4404 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is EN 1.4404 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19 to 20
14 to 43
Fatigue Strength, MPa 190 to 260
220 to 320
Impact Strength: V-Notched Charpy, J 23 to 38
91 to 93
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 350 to 390
420 to 550
Tensile Strength: Ultimate (UTS), MPa 560 to 620
600 to 900
Tensile Strength: Yield (Proof), MPa 280 to 380
240 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.8
Embodied Energy, MJ/kg 19
52
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
110 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
140 to 800
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20 to 22
21 to 32
Strength to Weight: Bending, points 19 to 21
20 to 26
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19 to 21
13 to 20

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0 to 0.4
16.5 to 18.5
Iron (Fe), % 97.4 to 99.18
62.8 to 71.5
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
2.0 to 2.5
Nickel (Ni), % 0 to 0.4
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.015