MakeItFrom.com
Menu (ESC)

EN 1.1181 Steel vs. SAE-AISI 1340 Steel

Both EN 1.1181 steel and SAE-AISI 1340 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is SAE-AISI 1340 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
160 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
11 to 23
Fatigue Strength, MPa 190 to 260
220 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 350 to 390
340 to 440
Tensile Strength: Ultimate (UTS), MPa 560 to 620
540 to 730
Tensile Strength: Yield (Proof), MPa 280 to 380
300 to 620

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
51
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
78 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
240 to 1040
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20 to 22
19 to 26
Strength to Weight: Bending, points 19 to 21
19 to 23
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19 to 21
17 to 23

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.38 to 0.43
Chromium (Cr), % 0 to 0.4
0
Iron (Fe), % 97.4 to 99.18
97.2 to 97.9
Manganese (Mn), % 0.5 to 0.8
1.6 to 1.9
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.035
0 to 0.040