EN 1.1181 Steel vs. SAE-AISI 4028 Steel

Both EN 1.1181 steel and SAE-AISI 4028 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.1181 steel and the bottom bar is SAE-AISI 4028 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 180
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19 to 20
14 to 23
Fatigue Strength, MPa 190 to 260
180 to 330
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350 to 390
310 to 380
Tensile Strength: Ultimate (UTS), MPa 560 to 620
490 to 630
Tensile Strength: Yield (Proof), MPa 280 to 380
260 to 520

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
49
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 110
81 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 380
180 to 720
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20 to 22
17 to 22
Strength to Weight: Bending, points 19 to 21
18 to 21
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 19 to 21
16 to 20

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.25 to 0.3
Chromium (Cr), % 0 to 0.4
0
Iron (Fe), % 97.4 to 99.18
98.1 to 98.7
Manganese (Mn), % 0.5 to 0.8
0.7 to 0.9
Molybdenum (Mo), % 0 to 0.1
0.2 to 0.3
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.035
0.035 to 0.050