EN 1.1203 Steel vs. EN 1.1133 Steel
Both EN 1.1203 steel and EN 1.1133 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.1203 steel and the bottom bar is EN 1.1133 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 230 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 15 | |
| 19 to 24 |
| Fatigue Strength, MPa | 210 to 310 | |
| 230 to 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 420 to 480 | |
| 370 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 780 | |
| 580 to 620 |
| Tensile Strength: Yield (Proof), MPa | 340 to 480 | |
| 320 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 49 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 100 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 610 | |
| 270 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 21 to 22 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 13 | |
| 13 |
| Thermal Shock Resistance, points | 22 to 25 | |
| 18 to 19 |
Alloy Composition
| Carbon (C), % | 0.52 to 0.6 | |
| 0.17 to 0.23 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 to 0.4 |
| Iron (Fe), % | 97.1 to 98.9 | |
| 96.9 to 98.8 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 1.0 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.035 |