EN 1.1244 Steel vs. ACI-ASTM CD6MN Steel

Both EN 1.1244 steel and ACI-ASTM CD6MN steel are iron alloys. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is ACI-ASTM CD6MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 72
80
Tensile Strength: Ultimate (UTS), MPa 730 to 770
730

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 19
48
Embodied Water, L/kg 47
170

Common Calculations

Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26 to 28
26
Strength to Weight: Bending, points 23 to 24
23
Thermal Diffusivity, mm2/s 14
4.4
Thermal Shock Resistance, points 23 to 25
20

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.65 to 0.75
0 to 0.060
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.1 to 99.2
62.1 to 70.1
Manganese (Mn), % 0.8 to 1.1
0 to 1.0
Molybdenum (Mo), % 0
1.8 to 2.5
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.15 to 0.25
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.040