EN 1.1244 Steel vs. AISI 410S Stainless Steel

Both EN 1.1244 steel and AISI 410S stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is AISI 410S stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 730 to 770
480

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
740
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
30
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 19
27
Embodied Water, L/kg 47
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26 to 28
17
Strength to Weight: Bending, points 23 to 24
18
Thermal Diffusivity, mm2/s 14
8.1
Thermal Shock Resistance, points 23 to 25
17

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.65 to 0.75
0 to 0.080
Chromium (Cr), % 0
11.5 to 13.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.1 to 99.2
83.8 to 88.5
Manganese (Mn), % 0.8 to 1.1
0 to 1.0
Nickel (Ni), % 0
0 to 0.6
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030