EN 1.1244 Steel vs. EN 1.6920 Steel

Both EN 1.1244 steel and EN 1.6920 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is EN 1.6920 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 730 to 770
640

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 47
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 28
22
Strength to Weight: Bending, points 23 to 24
21
Thermal Diffusivity, mm2/s 14
10
Thermal Shock Resistance, points 23 to 25
19

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.65 to 0.75
0 to 0.17
Chromium (Cr), % 0
0.5 to 1.0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.1 to 99.2
95.7 to 98
Manganese (Mn), % 0.8 to 1.1
1.0 to 1.5
Molybdenum (Mo), % 0
0.2 to 0.35
Nickel (Ni), % 0
0.3 to 0.7
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0
0.050 to 0.1