EN 1.1244 Steel vs. EN 1.7218 Steel

Both EN 1.1244 steel and EN 1.7218 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is EN 1.7218 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
150 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 730 to 770
500 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
44
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
52

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 28
18 to 55
Strength to Weight: Bending, points 23 to 24
18 to 38
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 23 to 25
15 to 46

Alloy Composition

Aluminum (Al), % 0 to 0.050
0 to 0.040
Carbon (C), % 0.65 to 0.75
0.22 to 0.29
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 98.1 to 99.2
96.2 to 98.1
Manganese (Mn), % 0.8 to 1.1
0.6 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 0
0 to 0.3
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035

Comparable Variants