EN 1.1244 Steel vs. Grade 7 Titanium

EN 1.1244 steel belongs to the iron alloys classification, while grade 7 titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is grade 7 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
150
Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
38
Tensile Strength: Ultimate (UTS), MPa 730 to 770
420

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Maximum Temperature: Mechanical, °C 400
320
Melting Completion (Liquidus), °C 1450
1660
Melting Onset (Solidus), °C 1410
1610
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 51
22
Thermal Expansion, µm/m-K 12
9.2

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
7.2

Otherwise Unclassified Properties

Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 1.4
47
Embodied Energy, MJ/kg 19
800
Embodied Water, L/kg 47
470

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 26 to 28
26
Strength to Weight: Bending, points 23 to 24
28
Thermal Diffusivity, mm2/s 14
8.9
Thermal Shock Resistance, points 23 to 25
31

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.65 to 0.75
0 to 0.080
Copper (Cu), % 0 to 0.3
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 98.1 to 99.2
0 to 0.3
Manganese (Mn), % 0.8 to 1.1
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0 to 0.0020
0 to 0.25
Palladium (Pd), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
98.7 to 99.88
Residuals, % 0
0 to 0.4