EN 1.1244 Steel vs. Grade C-5 Titanium

EN 1.1244 steel belongs to the iron alloys classification, while grade C-5 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is grade C-5 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
310
Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
40
Tensile Strength: Ultimate (UTS), MPa 730 to 770
1000

Thermal Properties

Latent Heat of Fusion, J/g 250
410
Maximum Temperature: Mechanical, °C 400
340
Melting Completion (Liquidus), °C 1450
1610
Melting Onset (Solidus), °C 1410
1560
Specific Heat Capacity, J/kg-K 470
560
Thermal Conductivity, W/m-K 51
7.1
Thermal Expansion, µm/m-K 12
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
36
Density, g/cm3 7.8
4.4
Embodied Carbon, kg CO2/kg material 1.4
38
Embodied Energy, MJ/kg 19
610
Embodied Water, L/kg 47
200

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 26 to 28
63
Strength to Weight: Bending, points 23 to 24
50
Thermal Diffusivity, mm2/s 14
2.9
Thermal Shock Resistance, points 23 to 25
71

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.050
5.5 to 6.8
Carbon (C), % 0.65 to 0.75
0 to 0.1
Copper (Cu), % 0 to 0.3
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 98.1 to 99.2
0 to 0.4
Manganese (Mn), % 0.8 to 1.1
0
Nickel (Ni), % 0
0 to 0.050
Oxygen (O), % 0 to 0.0020
0 to 0.25
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
87.5 to 91
Vanadium (V), % 0
3.5 to 4.5
Residuals, % 0
0 to 0.4