EN 1.1244 Steel vs. Titanium 6-2-4-2

EN 1.1244 steel belongs to the iron alloys classification, while titanium 6-2-4-2 belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is titanium 6-2-4-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
40
Tensile Strength: Ultimate (UTS), MPa 730 to 770
950

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 400
300
Melting Completion (Liquidus), °C 1450
1590
Melting Onset (Solidus), °C 1410
1540
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 51
6.9
Thermal Expansion, µm/m-K 12
9.5

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
0.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
42
Density, g/cm3 7.8
4.6
Embodied Carbon, kg CO2/kg material 1.4
32
Embodied Energy, MJ/kg 19
520
Embodied Water, L/kg 47
210

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
34
Strength to Weight: Axial, points 26 to 28
57
Strength to Weight: Bending, points 23 to 24
46
Thermal Diffusivity, mm2/s 14
2.8
Thermal Shock Resistance, points 23 to 25
67

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.050
5.5 to 6.5
Carbon (C), % 0.65 to 0.75
0 to 0.050
Copper (Cu), % 0 to 0.3
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 98.1 to 99.2
0 to 0.25
Manganese (Mn), % 0.8 to 1.1
0
Molybdenum (Mo), % 0
1.8 to 2.2
Nitrogen (N), % 0
0 to 0.050
Oxygen (O), % 0 to 0.0020
0 to 0.15
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0.060 to 0.12
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.8 to 2.2
Titanium (Ti), % 0
83.7 to 87.2
Zirconium (Zr), % 0
3.6 to 4.4
Residuals, % 0
0 to 0.4