EN 1.1244 Steel vs. K94200 Alloy

Both EN 1.1244 steel and K94200 alloy are iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is K94200 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
140
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 72
54
Tensile Strength: Ultimate (UTS), MPa 730 to 770
500 to 710

Thermal Properties

Melting Onset (Solidus), °C 1410
1440
Specific Heat Capacity, J/kg-K 470
500
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
5.0

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.0

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.2

Common Calculations

Stiffness to Weight: Axial, points 13
9.8
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 26 to 28
17 to 24
Strength to Weight: Bending, points 23 to 24
17 to 22
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 23 to 25
49 to 70