EN 1.1244 Steel vs. R30001 Cobalt

EN 1.1244 steel belongs to the iron alloys classification, while R30001 cobalt belongs to the cobalt alloys. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1244 steel and the bottom bar is R30001 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
86
Tensile Strength: Ultimate (UTS), MPa 730 to 770
620

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1450
1530
Melting Onset (Solidus), °C 1410
1260
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.8

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.4
8.9
Embodied Energy, MJ/kg 19
130
Embodied Water, L/kg 47
460

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 26 to 28
19
Strength to Weight: Bending, points 23 to 24
18
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 23 to 25
19

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.65 to 0.75
2.0 to 3.0
Chromium (Cr), % 0
28 to 32
Cobalt (Co), % 0
43 to 59
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.1 to 99.2
0 to 3.0
Manganese (Mn), % 0.8 to 1.1
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0
0 to 3.0
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0 to 2.0
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 0
11 to 13