EN 1.3505 Steel vs. EN 1.6526 Steel

Both EN 1.3505 steel and EN 1.6526 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.3505 steel and the bottom bar is EN 1.6526 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 210
160 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 600 to 690
520 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.6
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
20
Embodied Water, L/kg 52
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22 to 25
18 to 52
Strength to Weight: Bending, points 20 to 22
18 to 36
Thermal Diffusivity, mm2/s 12
10
Thermal Shock Resistance, points 18 to 20
15 to 43

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.93 to 1.1
0.17 to 0.23
Chromium (Cr), % 1.4 to 1.6
0.35 to 0.7
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 97.1 to 98.3
96.6 to 98.3
Manganese (Mn), % 0.25 to 0.45
0.65 to 1.0
Molybdenum (Mo), % 0 to 0.1
0.15 to 0.25
Nickel (Ni), % 0
0.4 to 0.7
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.030
0.020 to 0.040

Comparable Variants