EN 1.3538 Steel vs. S46910 Stainless Steel
Both EN 1.3538 steel and S46910 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.3538 steel and the bottom bar is S46910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 220 | |
| 270 to 630 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 740 | |
| 680 to 2470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 810 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.0 | |
| 18 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 4.1 |
| Embodied Energy, MJ/kg | 21 | |
| 55 |
| Embodied Water, L/kg | 56 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 3.3 | |
| 25 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 26 | |
| 24 to 86 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 22 to 51 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 23 to 84 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0.15 to 0.5 |
| Carbon (C), % | 0.93 to 1.1 | |
| 0 to 0.030 |
| Chromium (Cr), % | 1.7 to 2.0 | |
| 11 to 13 |
| Copper (Cu), % | 0 to 0.3 | |
| 1.5 to 3.5 |
| Iron (Fe), % | 96 to 97.2 | |
| 65 to 76 |
| Manganese (Mn), % | 0.6 to 0.8 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.4 to 0.5 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.5 to 1.2 |