EN 1.3539 Steel vs. CC760S Brass

EN 1.3539 steel belongs to the iron alloys classification, while CC760S brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.3539 steel and the bottom bar is CC760S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
51
Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
42
Tensile Strength: Ultimate (UTS), MPa 670
180

Thermal Properties

Latent Heat of Fusion, J/g 260
190
Maximum Temperature: Mechanical, °C 450
170
Melting Completion (Liquidus), °C 1450
1000
Melting Onset (Solidus), °C 1410
940
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 39
150
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
38
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
40

Otherwise Unclassified Properties

Base Metal Price, % relative 3.2
28
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.7
2.6
Embodied Energy, MJ/kg 22
43
Embodied Water, L/kg 57
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 24
5.8
Strength to Weight: Bending, points 22
8.2
Thermal Diffusivity, mm2/s 11
45
Thermal Shock Resistance, points 20
6.2

Alloy Composition

Aluminum (Al), % 0 to 0.050
0 to 0.010
Arsenic (As), % 0
0.050 to 0.15
Carbon (C), % 0.93 to 1.1
0
Chromium (Cr), % 1.8 to 2.1
0
Copper (Cu), % 0 to 0.3
83 to 88
Iron (Fe), % 95.2 to 96.5
0 to 0.15
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0.8 to 1.1
0 to 0.1
Molybdenum (Mo), % 0.5 to 0.6
0
Nickel (Ni), % 0
0 to 0.1
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.4 to 0.6
0 to 0.020
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
10.7 to 17