EN 1.3539 Steel vs. Grade 3 Babbitt Metal

EN 1.3539 steel belongs to the iron alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.3539 steel and the bottom bar is grade 3 Babbitt Metal.

EN 1.3539 (100CrMnMoSi8-4-6) Through-Hardening Bearing Steel Grade 3 (L13840) Tin-Base Babbitt Metal

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness		200
Brinell Hardness		27

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		56

Poisson's Ratio		0.29
Poisson's Ratio		0.35

Shear Modulus, GPa		73
Shear Modulus, GPa		21

Thermal Properties

Latent Heat of Fusion, J/g		260
Latent Heat of Fusion, J/g		79

Melting Completion (Liquidus), °C		1450
Melting Completion (Liquidus), °C		420

Melting Onset (Solidus), °C		1410
Melting Onset (Solidus), °C		240

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		230

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Base Metal Price, % relative		3.2
Base Metal Price, % relative		70

Density, g/cm³		7.8
Density, g/cm³		7.4

Embodied Carbon, kg CO₂/kg material		1.7
Embodied Carbon, kg CO₂/kg material		12

Embodied Energy, MJ/kg		22
Embodied Energy, MJ/kg		200

Embodied Water, L/kg		57
Embodied Water, L/kg		1210

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		4.2

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		17

Alloy Composition

Aluminum (Al), %		0 to 0.050
Aluminum (Al), %		0 to 0.0050

Antimony (Sb), %		0
Antimony (Sb), %		7.5 to 8.5

Arsenic (As), %		0
Arsenic (As), %		0 to 0.1

Bismuth (Bi), %		0
Bismuth (Bi), %		0 to 0.080

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Carbon (C), %		0.93 to 1.1
Carbon (C), %		0

Chromium (Cr), %		1.8 to 2.1
Chromium (Cr), %		0

Copper (Cu), %		0 to 0.3
Copper (Cu), %		7.5 to 8.5

Iron (Fe), %		95.2 to 96.5
Iron (Fe), %		0 to 0.080

Lead (Pb), %		0
Lead (Pb), %		0 to 0.35

Manganese (Mn), %		0.8 to 1.1
Manganese (Mn), %		0

Molybdenum (Mo), %		0.5 to 0.6
Molybdenum (Mo), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Phosphorus (P), %		0 to 0.025
Phosphorus (P), %		0

Silicon (Si), %		0.4 to 0.6
Silicon (Si), %		0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		82.3 to 85

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.0050