EN 1.3542 Stainless Steel vs. ASTM A387 Grade 11 Steel

Both EN 1.3542 stainless steel and ASTM A387 grade 11 steel are iron alloys. They have 88% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is ASTM A387 grade 11 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 720
500 to 600

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 770
430
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 29
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
2.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
1.6
Embodied Energy, MJ/kg 29
21
Embodied Water, L/kg 100
53

Common Calculations

PREN (Pitting Resistance) 15
3.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
18 to 21
Strength to Weight: Bending, points 23
18 to 20
Thermal Diffusivity, mm2/s 7.9
11
Thermal Shock Resistance, points 26
15 to 18

Alloy Composition

Carbon (C), % 0.6 to 0.7
0.050 to 0.17
Chromium (Cr), % 12.5 to 14.5
1.0 to 1.5
Iron (Fe), % 82.7 to 87.5
96.2 to 97.6
Manganese (Mn), % 0 to 1.0
0.4 to 0.65
Molybdenum (Mo), % 0 to 0.75
0.45 to 0.65
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.5 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025