EN 1.3542 Stainless Steel vs. EN 1.1152 Steel

Both EN 1.3542 stainless steel and EN 1.1152 steel are iron alloys. They have 86% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is EN 1.1152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 720
400 to 550

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 770
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 29
52
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
1.4
Embodied Energy, MJ/kg 29
18
Embodied Water, L/kg 100
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
14 to 19
Strength to Weight: Bending, points 23
15 to 19
Thermal Diffusivity, mm2/s 7.9
14
Thermal Shock Resistance, points 26
13 to 17

Alloy Composition

Carbon (C), % 0.6 to 0.7
0.18 to 0.22
Chromium (Cr), % 12.5 to 14.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 82.7 to 87.5
98.6 to 99.52
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.75
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025