EN 1.3542 Stainless Steel vs. EN 1.4110 Stainless Steel
Both EN 1.3542 stainless steel and EN 1.4110 stainless steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is EN 1.4110 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 720 | |
| 770 to 1720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 380 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 770 | |
| 790 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1440 |
| Melting Onset (Solidus), °C | 1390 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 29 | |
| 30 |
| Thermal Expansion, µm/m-K | 10 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.1 | |
| 2.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.6 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 8.0 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 2.3 |
| Embodied Energy, MJ/kg | 29 | |
| 33 |
| Embodied Water, L/kg | 100 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 15 | |
| 16 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 26 | |
| 28 to 62 |
| Strength to Weight: Bending, points | 23 | |
| 24 to 41 |
| Thermal Diffusivity, mm2/s | 7.9 | |
| 8.1 |
| Thermal Shock Resistance, points | 26 | |
| 27 to 60 |
Alloy Composition
| Carbon (C), % | 0.6 to 0.7 | |
| 0.48 to 0.6 |
| Chromium (Cr), % | 12.5 to 14.5 | |
| 13 to 15 |
| Iron (Fe), % | 82.7 to 87.5 | |
| 81.4 to 86 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0.5 to 0.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0 to 0.15 |