EN 1.3542 Stainless Steel vs. EN 1.4411 Stainless Steel

Both EN 1.3542 stainless steel and EN 1.4411 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is EN 1.4411 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 720
870

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Corrosion, °C 380
410
Maximum Temperature: Mechanical, °C 770
880
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 29
17
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
13
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.0
Embodied Energy, MJ/kg 29
41
Embodied Water, L/kg 100
130

Common Calculations

PREN (Pitting Resistance) 15
22
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
31
Strength to Weight: Bending, points 23
26
Thermal Diffusivity, mm2/s 7.9
4.6
Thermal Shock Resistance, points 26
28

Alloy Composition

Carbon (C), % 0.6 to 0.7
0 to 0.060
Chromium (Cr), % 12.5 to 14.5
15 to 17
Iron (Fe), % 82.7 to 87.5
73.1 to 79.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
1.5 to 2.0
Nickel (Ni), % 0
4.0 to 6.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025