EN 1.3542 Stainless Steel vs. EN 1.4419 Stainless Steel

Both EN 1.3542 stainless steel and EN 1.4419 stainless steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is EN 1.4419 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 720
660 to 1590

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Corrosion, °C 380
390
Maximum Temperature: Mechanical, °C 770
790
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 29
30
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
8.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.2
Embodied Energy, MJ/kg 29
30
Embodied Water, L/kg 100
110

Common Calculations

PREN (Pitting Resistance) 15
16
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
24 to 57
Strength to Weight: Bending, points 23
22 to 39
Thermal Diffusivity, mm2/s 7.9
8.1
Thermal Shock Resistance, points 26
23 to 55

Alloy Composition

Carbon (C), % 0.6 to 0.7
0.36 to 0.42
Chromium (Cr), % 12.5 to 14.5
13 to 14.5
Iron (Fe), % 82.7 to 87.5
82 to 86
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
0.6 to 1.0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015