EN 1.3542 Stainless Steel vs. EN 1.4948 Stainless Steel

Both EN 1.3542 stainless steel and EN 1.4948 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is EN 1.4948 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 720
610

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 380
410
Maximum Temperature: Mechanical, °C 770
930
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 29
17
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.0
Embodied Energy, MJ/kg 29
43
Embodied Water, L/kg 100
140

Common Calculations

PREN (Pitting Resistance) 15
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
22
Strength to Weight: Bending, points 23
21
Thermal Diffusivity, mm2/s 7.9
4.5
Thermal Shock Resistance, points 26
14

Alloy Composition

Carbon (C), % 0.6 to 0.7
0.040 to 0.080
Chromium (Cr), % 12.5 to 14.5
17 to 19
Iron (Fe), % 82.7 to 87.5
66.8 to 75
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0
8.0 to 11
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015