EN 1.3542 Stainless Steel vs. S33425 Stainless Steel

Both EN 1.3542 stainless steel and S33425 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is S33425 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 720
580

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 380
500
Maximum Temperature: Mechanical, °C 770
1100
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 29
14
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
27
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.0
5.1
Embodied Energy, MJ/kg 29
71
Embodied Water, L/kg 100
190

Common Calculations

PREN (Pitting Resistance) 15
30
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
20
Strength to Weight: Bending, points 23
19
Thermal Diffusivity, mm2/s 7.9
3.7
Thermal Shock Resistance, points 26
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0.6 to 0.7
0 to 0.080
Chromium (Cr), % 12.5 to 14.5
21 to 23
Iron (Fe), % 82.7 to 87.5
47.2 to 56.7
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.75
2.0 to 3.0
Nickel (Ni), % 0
20 to 23
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0.15 to 0.6