EN 1.3543 Stainless Steel vs. 296.0 Aluminum

EN 1.3543 stainless steel belongs to the iron alloys classification, while 296.0 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is 296.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
75 to 90
Elastic (Young's, Tensile) Modulus, GPa 200
72
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
27
Tensile Strength: Ultimate (UTS), MPa 730
260 to 270

Thermal Properties

Latent Heat of Fusion, J/g 280
420
Maximum Temperature: Mechanical, °C 870
170
Melting Completion (Liquidus), °C 1430
630
Melting Onset (Solidus), °C 1390
540
Specific Heat Capacity, J/kg-K 480
870
Thermal Conductivity, W/m-K 22
130 to 150
Thermal Expansion, µm/m-K 10
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
33 to 37
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
99 to 110

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
11
Density, g/cm3 7.7
3.0
Embodied Carbon, kg CO2/kg material 2.3
7.8
Embodied Energy, MJ/kg 32
150
Embodied Water, L/kg 120
1110

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
46
Strength to Weight: Axial, points 27
24 to 25
Strength to Weight: Bending, points 24
30 to 31
Thermal Diffusivity, mm2/s 6.1
51 to 56
Thermal Shock Resistance, points 26
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
89 to 94
Carbon (C), % 1.0 to 1.2
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
4.0 to 5.0
Iron (Fe), % 79.1 to 83.6
0 to 1.2
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0 to 1.0
0 to 0.35
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
0 to 0.35
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
2.0 to 3.0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.35