EN 1.3543 Stainless Steel vs. ASTM A369 Grade FP2

Both EN 1.3543 stainless steel and ASTM A369 grade FP2 are iron alloys. They have 83% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is ASTM A369 grade FP2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 730
430

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
49
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
2.6
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.6
Embodied Energy, MJ/kg 32
20
Embodied Water, L/kg 120
50

Common Calculations

PREN (Pitting Resistance) 19
2.5
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
15
Strength to Weight: Bending, points 24
16
Thermal Diffusivity, mm2/s 6.1
13
Thermal Shock Resistance, points 26
13

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.1 to 0.2
Chromium (Cr), % 16 to 18
0.5 to 0.81
Iron (Fe), % 79.1 to 83.6
97.4 to 98.6
Manganese (Mn), % 0 to 1.0
0.3 to 0.61
Molybdenum (Mo), % 0.4 to 0.8
0.44 to 0.65
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.1 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025