EN 1.3543 Stainless Steel vs. ASTM A369 Grade FP92

Both EN 1.3543 stainless steel and ASTM A369 grade FP92 are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is ASTM A369 grade FP92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 730
710

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 870
590
Melting Completion (Liquidus), °C 1430
1490
Melting Onset (Solidus), °C 1390
1450
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
26
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
10

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
11
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
2.8
Embodied Energy, MJ/kg 32
40
Embodied Water, L/kg 120
89

Common Calculations

PREN (Pitting Resistance) 19
14
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 24
22
Thermal Diffusivity, mm2/s 6.1
6.9
Thermal Shock Resistance, points 26
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 1.0 to 1.2
0.070 to 0.13
Chromium (Cr), % 16 to 18
8.5 to 9.5
Iron (Fe), % 79.1 to 83.6
85.8 to 89.1
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.4 to 0.8
0.3 to 0.6
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010