EN 1.3543 Stainless Steel vs. AWS BNi-1

EN 1.3543 stainless steel belongs to the iron alloys classification, while AWS BNi-1 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS BNi-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
180
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 76
70
Tensile Strength: Ultimate (UTS), MPa 730
450

Thermal Properties

Latent Heat of Fusion, J/g 280
360
Melting Completion (Liquidus), °C 1430
1040
Melting Onset (Solidus), °C 1390
980
Specific Heat Capacity, J/kg-K 480
500
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
55
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.3
8.8
Embodied Energy, MJ/kg 32
120
Embodied Water, L/kg 120
240

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
16
Strength to Weight: Bending, points 24
16
Thermal Shock Resistance, points 26
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
2.8 to 3.5
Carbon (C), % 1.0 to 1.2
0.6 to 0.9
Chromium (Cr), % 16 to 18
13 to 15
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 79.1 to 83.6
4.0 to 5.0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
69.8 to 75.7
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 1.0
4.0 to 5.0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5