EN 1.3543 Stainless Steel vs. AWS BNi-11

EN 1.3543 stainless steel belongs to the iron alloys classification, while AWS BNi-11 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS BNi-11.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 76
74
Tensile Strength: Ultimate (UTS), MPa 730
600

Thermal Properties

Latent Heat of Fusion, J/g 280
340
Melting Completion (Liquidus), °C 1430
1100
Melting Onset (Solidus), °C 1390
970
Specific Heat Capacity, J/kg-K 480
450
Thermal Expansion, µm/m-K 10
11

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
75
Density, g/cm3 7.7
9.1
Embodied Carbon, kg CO2/kg material 2.3
11
Embodied Energy, MJ/kg 32
160
Embodied Water, L/kg 120
230

Common Calculations

Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 27
18
Strength to Weight: Bending, points 24
17
Thermal Shock Resistance, points 26
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
2.2 to 3.1
Carbon (C), % 1.0 to 1.2
0.3 to 0.5
Chromium (Cr), % 16 to 18
9.0 to 11.8
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 79.1 to 83.6
2.5 to 4.0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
62.9 to 71.2
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 1.0
3.4 to 4.3
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
11.5 to 12.8
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5