EN 1.3543 stainless steel belongs to the iron alloys classification, while AWS BNi-6 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS BNi-6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
160
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 76
62
Tensile Strength: Ultimate (UTS), MPa 730
450

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Melting Completion (Liquidus), °C 1430
880
Melting Onset (Solidus), °C 1390
880
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
9.8

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
55
Density, g/cm3 7.7
8.2
Embodied Carbon, kg CO2/kg material 2.3
9.4
Embodied Energy, MJ/kg 32
130
Embodied Water, L/kg 120
210

Common Calculations

Stiffness to Weight: Axial, points 14
11
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 27
15
Strength to Weight: Bending, points 24
16
Thermal Shock Resistance, points 26
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 1.0 to 1.2
0 to 0.060
Chromium (Cr), % 16 to 18
0
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 79.1 to 83.6
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
87.2 to 90
Phosphorus (P), % 0 to 0.040
10 to 12
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5