EN 1.3543 Stainless Steel vs. AWS E219

Both EN 1.3543 stainless steel and AWS E219 are iron alloys. They have 81% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS E219.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 730
690

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 22
14
Thermal Expansion, µm/m-K 10
15

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
15
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.3
3.1
Embodied Energy, MJ/kg 32
44
Embodied Water, L/kg 120
160

Common Calculations

PREN (Pitting Resistance) 19
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 24
23
Thermal Diffusivity, mm2/s 6.1
3.8
Thermal Shock Resistance, points 26
17

Alloy Composition

Carbon (C), % 1.0 to 1.2
0 to 0.060
Chromium (Cr), % 16 to 18
19 to 21.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 79.1 to 83.6
58.6 to 67.4
Manganese (Mn), % 0 to 1.0
8.0 to 10
Molybdenum (Mo), % 0.4 to 0.8
0 to 0.75
Nickel (Ni), % 0
5.5 to 7.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030