EN 1.3543 Stainless Steel vs. AWS E310

Both EN 1.3543 stainless steel and AWS E310 are iron alloys. They have 68% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS E310.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 730
620

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 22
14
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
26
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
4.6
Embodied Energy, MJ/kg 32
65
Embodied Water, L/kg 120
200

Common Calculations

PREN (Pitting Resistance) 19
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
22
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 6.1
3.7
Thermal Shock Resistance, points 26
15

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.080 to 0.2
Chromium (Cr), % 16 to 18
25 to 28
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 79.1 to 83.6
44.5 to 53.9
Manganese (Mn), % 0 to 1.0
1.0 to 2.5
Molybdenum (Mo), % 0.4 to 0.8
0 to 0.75
Nickel (Ni), % 0
20 to 22.5
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030