EN 1.3543 Stainless Steel vs. AWS E349

Both EN 1.3543 stainless steel and AWS E349 are iron alloys. They have 84% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is AWS E349.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 730
770

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
15
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
4.9
Embodied Energy, MJ/kg 32
72
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 19
24
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
27
Strength to Weight: Bending, points 24
24
Thermal Diffusivity, mm2/s 6.1
4.1
Thermal Shock Resistance, points 26
20

Alloy Composition

Carbon (C), % 1.0 to 1.2
0 to 0.13
Chromium (Cr), % 16 to 18
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 79.1 to 83.6
60.5 to 71.1
Manganese (Mn), % 0 to 1.0
0.5 to 2.5
Molybdenum (Mo), % 0.4 to 0.8
0.35 to 0.65
Nickel (Ni), % 0
8.0 to 10
Niobium (Nb), % 0
0.75 to 1.2
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.15
Tungsten (W), % 0
1.3 to 1.8
Vanadium (V), % 0
0.1 to 0.3