EN 1.3543 Stainless Steel vs. EN 1.0258 Steel

Both EN 1.3543 stainless steel and EN 1.0258 steel are iron alloys. They have 82% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 730
490

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
49
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
2.1
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.5
Embodied Energy, MJ/kg 32
19
Embodied Water, L/kg 120
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
17
Strength to Weight: Bending, points 24
18
Thermal Diffusivity, mm2/s 6.1
13
Thermal Shock Resistance, points 26
16

Alloy Composition

Carbon (C), % 1.0 to 1.2
0 to 0.2
Chromium (Cr), % 16 to 18
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 79.1 to 83.6
96.9 to 100
Manganese (Mn), % 0 to 1.0
0 to 1.4
Molybdenum (Mo), % 0.4 to 0.8
0 to 0.080
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020