EN 1.3543 Stainless Steel vs. EN 1.4980 Stainless Steel

Both EN 1.3543 stainless steel and EN 1.4980 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is EN 1.4980 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
75
Tensile Strength: Ultimate (UTS), MPa 730
1030

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
780
Maximum Temperature: Mechanical, °C 870
920
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
13
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
26
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.3
6.0
Embodied Energy, MJ/kg 32
87
Embodied Water, L/kg 120
170

Common Calculations

PREN (Pitting Resistance) 19
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
36
Strength to Weight: Bending, points 24
28
Thermal Diffusivity, mm2/s 6.1
3.5
Thermal Shock Resistance, points 26
22

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 1.0 to 1.2
0.030 to 0.080
Chromium (Cr), % 16 to 18
13.5 to 16
Iron (Fe), % 79.1 to 83.6
49.2 to 58.5
Manganese (Mn), % 0 to 1.0
1.0 to 2.0
Molybdenum (Mo), % 0.4 to 0.8
1.0 to 1.5
Nickel (Ni), % 0
24 to 27
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
1.9 to 2.3
Vanadium (V), % 0
0.1 to 0.5