EN 1.3543 Stainless Steel vs. EN 1.6553 Steel

Both EN 1.3543 stainless steel and EN 1.6553 steel are iron alloys. They have 83% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is EN 1.6553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
210 to 240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 730
710 to 800

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
2.7
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.6
Embodied Energy, MJ/kg 32
21
Embodied Water, L/kg 120
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
25 to 28
Strength to Weight: Bending, points 24
23 to 24
Thermal Diffusivity, mm2/s 6.1
10
Thermal Shock Resistance, points 26
21 to 23

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.23 to 0.28
Chromium (Cr), % 16 to 18
0.4 to 0.8
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 79.1 to 83.6
95.6 to 98.2
Manganese (Mn), % 0 to 1.0
0.6 to 1.0
Molybdenum (Mo), % 0.4 to 0.8
0.15 to 0.3
Nickel (Ni), % 0
0.4 to 0.8
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0 to 0.030