EN 1.3543 Stainless Steel vs. SAE-AISI 1042 Steel

Both EN 1.3543 stainless steel and SAE-AISI 1042 steel are iron alloys. They have 82% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is SAE-AISI 1042 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
180 to 200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 730
620 to 700

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 22
52
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 32
18
Embodied Water, L/kg 120
46

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
22 to 25
Strength to Weight: Bending, points 24
21 to 22
Thermal Diffusivity, mm2/s 6.1
14
Thermal Shock Resistance, points 26
20 to 22

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.4 to 0.47
Chromium (Cr), % 16 to 18
0
Iron (Fe), % 79.1 to 83.6
98.5 to 99
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0.4 to 0.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050