EN 1.3543 Stainless Steel vs. N06045 Nickel

EN 1.3543 stainless steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have 41% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is N06045 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 730
690

Thermal Properties

Latent Heat of Fusion, J/g 280
350
Maximum Temperature: Mechanical, °C 870
1010
Melting Completion (Liquidus), °C 1430
1350
Melting Onset (Solidus), °C 1390
1300
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
13

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
42
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.3
6.9
Embodied Energy, MJ/kg 32
98
Embodied Water, L/kg 120
250

Common Calculations

PREN (Pitting Resistance) 19
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
24
Strength to Weight: Bending, points 24
22
Thermal Shock Resistance, points 26
18

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 16 to 18
26 to 29
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 79.1 to 83.6
21 to 25
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
45 to 50.4
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
2.5 to 3.0
Sulfur (S), % 0 to 0.030
0 to 0.010