EN 1.3543 Stainless Steel vs. N08810 Stainless Steel

Both EN 1.3543 stainless steel and N08810 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3543 stainless steel and the bottom bar is N08810 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 730
520

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
490
Maximum Temperature: Mechanical, °C 870
1100
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1390
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 22
12
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
30
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.3
5.3
Embodied Energy, MJ/kg 32
76
Embodied Water, L/kg 120
200

Common Calculations

PREN (Pitting Resistance) 19
21
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
18
Strength to Weight: Bending, points 24
18
Thermal Diffusivity, mm2/s 6.1
3.0
Thermal Shock Resistance, points 26
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 1.0 to 1.2
0.050 to 0.1
Chromium (Cr), % 16 to 18
19 to 23
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 79.1 to 83.6
39.5 to 50.7
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.4 to 0.8
0
Nickel (Ni), % 0
30 to 35
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6