EN 1.3549 Stainless Steel vs. S20432 Stainless Steel

Both EN 1.3549 stainless steel and S20432 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is S20432 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 730
580

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 400
410
Maximum Temperature: Mechanical, °C 910
900
Melting Completion (Liquidus), °C 1430
1410
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 10
13
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 37
38
Embodied Water, L/kg 130
140

Common Calculations

PREN (Pitting Resistance) 22
20
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
21
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 5.6
4.0
Thermal Shock Resistance, points 26
13

Alloy Composition

Carbon (C), % 0.85 to 1.0
0 to 0.080
Chromium (Cr), % 17 to 19
17 to 18
Copper (Cu), % 0
2.0 to 3.0
Iron (Fe), % 77.5 to 82
66.7 to 74
Manganese (Mn), % 0 to 1.0
3.0 to 5.0
Molybdenum (Mo), % 0.9 to 1.3
0
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.070 to 0.12
0