EN 1.3549 Stainless Steel vs. S31060 Stainless Steel

Both EN 1.3549 stainless steel and S31060 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.3549 stainless steel and the bottom bar is S31060 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 730
680

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 400
440
Maximum Temperature: Mechanical, °C 910
1080
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
18
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
3.4
Embodied Energy, MJ/kg 37
48
Embodied Water, L/kg 130
170

Common Calculations

PREN (Pitting Resistance) 22
26
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
24
Strength to Weight: Bending, points 24
22
Thermal Diffusivity, mm2/s 5.6
4.0
Thermal Shock Resistance, points 26
15

Alloy Composition

Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0.85 to 1.0
0.050 to 0.1
Cerium (Ce), % 0
0 to 0.070
Chromium (Cr), % 17 to 19
22 to 24
Iron (Fe), % 77.5 to 82
61.4 to 67.8
Lanthanum (La), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.3
0
Nickel (Ni), % 0
10 to 12.5
Nitrogen (N), % 0
0.18 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.070 to 0.12
0