EN 1.3551 Steel vs. EN 1.5520 Steel
Both EN 1.3551 steel and EN 1.5520 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.3551 steel and the bottom bar is EN 1.5520 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 120 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 720 | |
| 410 to 1410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 530 | |
| 400 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1460 |
| Melting Onset (Solidus), °C | 1450 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 36 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.6 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.9 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 71 | |
| 19 |
| Embodied Water, L/kg | 82 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 15 to 50 |
| Strength to Weight: Bending, points | 23 | |
| 16 to 36 |
| Thermal Diffusivity, mm2/s | 9.8 | |
| 13 |
| Thermal Shock Resistance, points | 21 | |
| 12 to 41 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.77 to 0.85 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 88.8 to 91.1 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 0.15 to 0.35 | |
| 0.9 to 1.2 |
| Molybdenum (Mo), % | 4.0 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 to 0.25 | |
| 0 |
| Vanadium (V), % | 0.9 to 1.1 | |
| 0 |